Ceramic Fiber Insulation Board (2300F) (1" X 23.6" X 23.6") Pack of Individual Board for Wood Ovens, Stoves, Forges, Kilns, Furnaces

Aluminosilicate Refractory Ceramic Fiber Board-MADE IN INDIA.
Maximum Use Temperature: 2300 F(1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation – 78 PSI.
Permanent Linier Shrinkage – 3.5% Max at 2200 F when exposed to 24 hours soaking heat.

Aluminosilicate Refractory Ceramic Fiber Board-MADE IN INDIA.
Maximum Use Temperature: 2600 F(1425 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation – 78 PSI.
Permanent Linier Shrinkage – 3.5% Max at 2200 F when exposed to 24 hours soaking heat.

Aluminosilicate Refractory Ceramic Fiber Board-MADE IN INDIA.
Maximum Use Temperature: 2300 F(1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation – 78 PSI.
Permanent Linier Shrinkage – 3.5% Max at 2200 F when exposed to 24 hours soaking heat.

Aluminosilicate Refractory Ceramic Fiber Board-MADE IN INDIA.
Maximum Use Temperature: 2300 F(1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation – 78 PSI.
Permanent Linier Shrinkage – 3.5% Max at 2200 F when exposed to 24 hours soaking heat.

Aluminosilicate Refractory Ceramic Fiber Board-MADE IN INDIA.
Maximum Use Temperature: 2300 F(1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation – 78 PSI.
Permanent Linier Shrinkage – 3.5% Max at 2200 F when exposed to 24 hours soaking heat.

Aluminosilicate Refractory Ceramic Fiber Board-MADE IN INDIA.
Maximum Use Temperature: 2300 F(1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation – 78 PSI.
Permanent Linier Shrinkage – 3.5% Max at 2200 F when exposed to 24 hours soaking heat.

Aluminosilicate Refractory Ceramic Fiber Board measures 1” X 18” X 24” in size..
Maximum Use Temperature: 2300 F (1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation - 78 PSI, Permanent Linier Shrinkage - 3.5% Max at 2200 F when exposed to 24 hours soaking heat, Loss of Ignition(LOI) at 1832 F : 4-7.
Easy to cut: This Board can be easily cut with knife & hacksaw blade and can be drilled and machined. This board is not as strong as firebrick, it dents easily..
Uses: High temperature Board is used to repair or build, Wood Stove, Fireplaces, Pizza Ovens, Kilns, Forges, Internal Baffle of Wood Stove, Pellet Stove, Backup Insulation of Refractory Bricks and Castable Linings, Furnace Hot Face Linings and Boiler Wall Insulation, heat shields, combustion chambers and fire protection. Commonly used to make target walls, front plates and floor insulation..

Aluminosilicate Refractory Ceramic Fiber Board measures 1” X 18” X 24” in size..
Maximum Use Temperature: 2300 F (1260 C) | Density: 20-24 lb/ft³.
Compressive Strength at 25% deformation - 78 PSI, Permanent Linier Shrinkage - 3.5% Max at 2200 F when exposed to 24 hours soaking heat, Loss of Ignition(LOI) at 1832 F : 4-7.
Easy to cut: This Board can be easily cut with knife & hacksaw blade and can be drilled and machined. This board is not as strong as firebrick, it dents easily..
Uses: High temperature Board is used to repair or build, Wood Stove, Fireplaces, Pizza Ovens, Kilns, Forges, Internal Baffle of Wood Stove, Pellet Stove, Backup Insulation of Refractory Bricks and Castable Linings, Furnace Hot Face Linings and Boiler Wall Insulation, heat shields, combustion chambers and fire protection. Commonly used to make target walls, front plates and floor insulation..

★Material: Ceramic ceramic fiber paper refers to industrial products made of ceramic fiber as raw materials, which are light in weight, high in temperature resistance, good in thermal stability, and easy to wear in an environment..
★Size: 21x29cm/8.2x11.6 inches, 1mm thick, can be cut into a suitable size with scissors, convenient and easy to use enough to meet your various process needs.
★Asbestos-free: All our products are asbestos-free. If used properly, they may be safer for humans and more environmentally friendly. For additional precautions for handling any ceramic fibers,.
★Quality structure: It is made of ceramic fiber, has low thermal conductivity and quality, and can resist thermal shock. It has the best quality and stability for a wide range of applications..
★Products are used for wooden stoves, baffles, fireplaces, stoves, pellet stoves, chimneys, boilers, pizza ovens, brazing, welding, welding, casting, pottery kilns, refractory materials, glass blowing, etc..